 Park Advanced Composite Materials Product Overview
E-765 Epoxy Prepregs
Park’s E‐765 is a toughened 270°F cure epoxy prepreg system designed to replace 350°F cure systems in many aircraft structural applications. Park’s E‐765‐3K‐PW, ‐6K‐5HS and 7781 materials are AGATE approved. FAA‐approved, B‐Basis design allowable databases for AGATE materials are available upon request. Park has also developed AGATE approved material and process specifications which are also available upon request. Key Features & Benefits -
Applications / Qualifications  Primary Aircraft Structures  Fuselage  Wing  Control Surfaces  Secondary Aircraft Structures  Fairings  Doors  Radomes  Bulkheads Designed to replace first generation 350°F (176°C) cure systems. Wide cure temperature process window of 260°F to 350°F (lower cures are possible depending on the application) Exhibits low void content, e.g., <2% after oven/vacuum cure. Excellent fiber property translation. 180°F Wet service temperature after ~270°F cure Good tack and drape characteristics after 30 days at room temperature Product Forms ‐ ‐ ‐ ‐ Available on a wide variety of reinforcements including fiberglass and carbon Various Fabrics per customer requirements (e.g., plain, harness and twill weaves) Unitape and glass broad goods up to 60 inches wide Compatible with autoclave, vacuum bag/oven or press cure processes Global Availability For Information about Park’s materials: Americas Asia Pacific Europe +1.316.283.6500 +656.861.7117 +33‐562‐985290 [email protected] www.parkelectro.com
Page 1 of 5 Rev. 10_12 Park Advanced Composite Materials Technical Datasheet E-765 Epoxy Prepregs
Nominal Prepreg and Laminate Physical Properties
T700
Uni Tape
150
35±3
1.0
18±6
Medium
Reinforcement
Fiber Areal Weight (gsm)
Resin Solids (%)
Volatile Content (% Max)
Flow – 275F @ 15psi (%)
Tack
Tg (dry, by DMA, onset storage mod.)
Gel time @ 275F (min)
Cure per ply thickness (in.)
3K PW
7781
E-Glass
303
38
1.0
20±6
Light-Medium
6K 5HS
193
370
38±3
40±3
1.0
1.0
20±6
20±6
Medium
Medium
150° C / 300°F
2-6
2-6
0.0089
0.0152
2-6
0.0056
2-6
0.0098
Nominal Prepreg and Laminate Physical Properties
Reinforcement
Fiber Areal Weight (gsm)
Resin Solids (%)
Volatile Content (% Max)
Flow – 275F @ 15psi (%)
Tack
Tg (dry, by DMA)
Gel time @ 275F (min)
Cure per ply thickness (in.)
12K 2x2
Twill
370
40 +/- 3
1.0
20±6
Light Medium
12K 2x2
Twill
670
40 +/-3
1.0
20±6
Light-Medium
2-6
0.015
2-6
0.022
12k 2x2
BW
635
35 +/-3
1.0
20±6
Light -Medium
120
E-Glass
107
45
1.0
20±6
Medium
165° C / 330°F
2–6
0.023
2-6
0.005
Selected Laminate Electrical Properties
Reinforcement
E-765 w/ E-Glass
E-765 w/ Quartz
Frequency
Dielectric Constant (Dk)
Loss Tangent (Df)
9.375 GHz
9.375 GHz
4.5
3.4
0.020
0.015
Sandwich Panel Properties
Reinforcement
E-765 w/ T300
3KPW
Property
Test Method
Mean Value
Climbing Drum Peel
Flatwise Tensile Strength
ASTM-D-1781
ASTM-C-297
4 in lb/in
1000 psi
All test data provided are typical values and not intended to be specification values. For review of critical specification tolerances, please
contact a Park representative directly. Park reserves the right to change these typical values as a natural process of refining our testing
equipment and techniques.
Page 2 of 5 Rev. 10_12 Park Advanced Composite Materials E-765 Epoxy Prepregs
Technical Datasheet Laminate Mechanical Properties - Carbon
Reinforcement
Fiber Areal Weight (gsm)
Cure Type
Tensile Strength, 0° (Ksi)
-65°F
Dry
70°F
Dry
180°F
Dry
180°F
Wet
T700
Uni Tape
150
T300
3K PW
193
T300
6K 5HS
370
T300
6K 5HS
370
Vacuum/Oven
Vacuum/Oven
Vacuum/Oven
Autoclave
370
370
349
333
93
95
93
96
89
86
98
--
91
100
100
100
18.8
18.7
18.2
18.6
8.5
8.2
7.9
8.0
9.5
9.3
9.0
--
9.9
9.3
9.2
8.9
211
180
177
107
109
96
77
57
127
114
83
--
125
115
82
64
17.9
18.1
18.4
18.0
7.8
7.7
7.5
7.5
10.3
8.8
8.9
--
10.1
8.9
8.8
8.5
17
13
9.
6
11
10
8
5
-11
---
-12
---
26
20
16
11
21
19
14
11
-----
21
18
15
10
ASTM-D-3039-95
Tensile Modulus (Msi)
-65°F
Dry
70°F
Dry
180°F
Dry
180°F
Wet
ASTM-D-3039-95
Compressive Strength (Ksi)
-65°F
Dry
70°F
Dry
180°F
Dry
180°F
Wet
SACMA 1-94
Compressive Modulus (Msi)
-65°F
Dry
70°F
Dry
180°F
Dry
180°F
Wet
SACMA 1-94
Short Beam Shear (Ksi)
-65°F
Dry
70°F
Dry
180°F
Dry
180°F
Wet
ASTM-D-2344
In-plane Shear Strength,
V-notched (Ksi)
-65°F
Dry
70°F
Dry
180°F
Dry
180°F
Wet
ASTM-D-5379-93
All test data provided are typical values and not intended to be specification values. For review of critical specification
tolerances, please contact a Park representative directly. Park reserves the right to change these typical values as a natural
process of refining our testing equipment and techniques.
Page 3 of 5 Rev. 10_12 Park Advanced Composite Materials E-765 Epoxy Prepregs
Technical Datasheet Laminate Mechanical Properties - Glass
Reinforcement
Fiber Areal Weight (gsm)
Cure Type
Tensile Strength, 0° (Ksi)
-65°F
Dry
70°F
Dry
180°F
Dry
180°F
Wet
120
E-Glass
107
7781
E-Glass
300
Vacuum/Oven
Vacuum/Oven
-53
---
73
65
61
50
-2.4
---
3.9
3.7
3.6
3.4
-63
---
85
73
61
52
-2.6
---
4.1
3.8
3.7
3.7
-9
---
10
8
7
5
-----
24
18
15
11
ASTM-D-3039-95
Tensile Modulus (Msi)
-65°F
Dry
70°F
Dry
180°F
Dry
180°F
Wet
ASTM-D-3039-95
Compressive Strength (Ksi)
-65°F
Dry
70°F
Dry
180°F
Dry
180°F
Wet
SACMA 1-94
Compressive Modulus (Msi)
-65°F
Dry
70°F
Dry
180°F
Dry
180°F
Wet
SACMA 1-94
Short Beam Shear (Ksi)
-65°F
Dry
70°F
Dry
180°F
Dry
180°F
Wet
ASTM-D-2344
In-plane Shear Strength,
notched (Ksi)
-65°F
Dry
70°F
Dry
180°F
Dry
180°F
Wet
V-
ASTM-D-5379-93
All test data provided are typical values and not intended to be specification values. For review of critical specification
tolerances, please contact a Park representative directly. Park reserves the right to change these typical values as a natural
process of refining our testing equipment and techniques.
Page 4 of 5 Rev. 10_12 Park Advanced Composite Materials E-765 Epoxy Prepregs
Processing Guidelines
Prepreg Storage Life
Out Life: 30 days @ 75°F Shelf Life: 6 months @ 0°F Tack Life: 21 days @ 75°F Note: The following guidelines are provided to assist Park material
users with general recommendations for successful processing. The
recommendations are for general review purposes only and process
adjustments may be required to achieve optimum results in your
specific manufacturing environment.
Autoclave Cure Cycle ‐ Apply 24”Hg vacuum (minimum) for a minimum of 1 hour before cure ‐ Apply 40 ‐100 psi autoclave pressure, vent vacuum when pressure reaches 15 – 20 psi ‐ Ramp product temp to 270‐280°F at 1 – 5° F (0.05 – 3°C)/min ‐ For Laminates > 0.125” thick, hold at 180°F for 60 minutes ‐ Hold product at 270‐280°F for 110‐130 minutes ‐ Cool to 150°F at 3 – 10°F/min prior to releasing autoclave pressure Vacuum/Oven Cure Cycle ‐ Apply 25”Hg vacuum (minimum) for a minimum of 1 hour before cure ‐ Ramp product temp to 270‐280°F at 1 – 5° F (0.05 – 3°C)/min ‐ For laminates > 0.125” thick, hold at 180°F for 60 minutes ‐ Hold product at 270‐280°F for 110‐130 minutes ‐ Cool to 150°F at 3 – 10°F/min Thick Laminate Cure Cycle - Slower ramp rate and multiple dwell times below 190°F are critical to remove excess energy from the system and avoid dangerous exotherms. - Contact your Park representative to discuss specific part process requirements to optimize processing of E‐765. - Failure to properly control the exotherm can lead to a potential safety hazard and/or degradation of final material performance. All test data provided are typical values and not intended to be specification values. For review of critical specification
tolerances, please contact a company representative directly. The above processing guides are recommendations only and
intended for general review purposes. Process adjustments may be required to achieve optimum results in your specific
manufacturing environment.
Park Electrochemical Corp. reserves the right to make changes without notice to any products described herein. Park does
not assume any liability arising out of the application or use of any product descried herein; and it does not grant any license
under its patent or other rights or any such rights of others. Park also disclaims all warranties whether expressed, implied or
statutory, including implied warranties of merchantability or fitness for a particular purpose.
Aeroglide™, CoreFix®, Easycure™, Nelco®, Nelcote®, Nova™, PeelCote™ and Powerbond™ are trademarks of Park
Electrochemical Corp.
Page 5 of 5 Rev. 10_12 